Stainless Steel Lockset Parts Plug Manufacturer

Technics: MIM
Quoted Condition: 2D / 3D Drawing / Sample
Package: Carton, Plastic Bag, Export Package
OEM/ODM: Welcome
Production Time: 15-30 Days
Weight: 24.8g
Size: 102.5*10.4 mm
Trademark: drome
Transport Package: Carton
Specification: 290*190
Origin: Suzhou, China
Technics: MIM
Quoted Condition: 2D / 3D Drawing / Sample
Package: Carton, Plastic Bag, Export Package
OEM/ODM: Welcome
Production Time: 15-30 Days
Weight: 24.8g
Size: 102.5*10.4 mm
Trademark: drome
Transport Package: Carton
Specification: 290*190
Origin: Suzhou, China
MIM(Metal powder Injection Molding) isthe5th generation of metal forming technology.  Over 40 years of development, people gradually find more applications for MIM process especially in the 3C products application. From initial groping to mature stage, MIM technology witness the ups and downs of 3C products in the past ten years.
Fortunately, there are several parts of design such as hinges, fiber optic connector bases, and new style connectors are closely dependent on MIM technology. These products are being produced in a large number and MIM technology is being adopted by more and more.


MIM and CIM--Drome can provide one-stop service solution.
The basic attributes include:
1.Economical production of complex parts with weight from 0.03 to 200g from high-performance engineering materials.
2.Parts with high dimensional precision (±0.1%~±0.5%) and good surface quality (surface roughness 1~2μm).
3.Parts with high relative density (96%~100%), homogeneous microstructure and superior performance.
4.Adaptable to powders of various materials and wide application of the parts.
5.Material saving through the recycle of wastes, production process with high level of automation and suitable for mass production

Flow chart of metal injection molding

Stainless Steel Lockset Parts Plug Manufacturer


Application of MIM
Stainless Steel Lockset Parts Plug Manufacturer






Products Range:
 
Material   Typical Values    
Designation Code Density g/cm3 Tensile Properties Young's modulus, Gpa Un-notched Charpy Impact Energy,J Hardness,Rockwell
    UTS. Mpa Y.S. (0.2%), Mpa Elongation (in 25.4mm) %     Macro (apparent)  Micro (converted)
MIM-Fe2Ni 7.8 280 115 25     55 HRB 50HRC    
MIM-Fe8Ni 7.8 450   12     84HRB 50HRC    
MIM-2200 (as sintered) 7.8 290 125 40.0 190 135 45 HRB  
MIM-2700 (as sintered) 7.8 415 255 26.0 190 175 69 HRB  
MIM-4605 (as sintered) 7.8 440 205 15.0 200 70 62 HRB  
MIM-4605 (Q&T) 7.8 1655 1480 2.0 205 55 48 HRC 55 HRC
MIM-304L 7.8 500   70     60 HRB  
MIM-316L (as sintered) 7.85 520 175 50.0 190 190 67 HRB  
MIM-410 7.7 900   7       40 HRC
MIM-420 (heat treated) 7.7 1380 1200 12 190 40   45-60HRC
MIM-430L (as sintered) 7.8 410 240 25.0 210 150 65 HRB  
MIM-440C 7.8 700 590 15       45-60HRC
MIM-17-4PH (as sintered) 7.8 900 730 6.0 190 140 27 HRC  
MIM-17-4PH (heat treated) 7.8 1190