Various products Bicycle Pump, pump, Tire Pump, floor pump,Hand Pump, Stainless Steel Pump, Mini Pump , inflator for children bicycle, bicycle, motorcycle, providing product images and basic parameters with each Various of bicycle pump, pump, tire pump, floor pump,hand pump, stalnless steel pump, mini pump, inflator for Children Bicycle / Bike / cycle / Bicycle part and motorcycle; We are a professional Chinese manufacturer of pump, tire pump, floor pump,hand pump, stalnless steel pump, mini pump, inflator, and look forward to your cooperation! Bicycle Pump Bicycle Pump,Tire Pump,Hand Pump,Stainless Steel Pump,Mini Pump SHIJIAZHUANG LONGXUAN TRADING CO., LTD , https://www.longxuanmachines.com
Valve corrosion, usually understood as the valve metal material under the chemical or electrochemical environment suffered damage. As "corrosion" occurs in the spontaneous interaction between metal and the surrounding environment, how to separate metals from the surrounding environment or use more non-metallic synthetic materials has become a common concern.
As we all know, metal corrosion damage to the valve's duration, reliability and service life have a considerable impact. The effect of mechanical and corrosion factors on the metal greatly increases the total amount of contact surface wear. Valve in operation, the total amount of wear on the surface of the friction. During operation of the valve, the frictional surface is subject to wear and tear as a result of simultaneous mechanical action and chemical or electrochemical interaction of the metal with the environment. For valves, the climatic conditions of the pipeline work are complicated; the presence of hydrogen sulfide, carbon dioxide and certain organic acids in media such as oil, natural gas and formation water increases the destructive power of their metal surfaces and rapidly loses their ability to work.
As the metal's chemical corrosion depends on the temperature, the mechanical load on the friction parts, the sulfide contained in the lubricating material and its acid resistance, the duration of contact with the medium and the catalytic effect of the metal on the nitriding process, Material molecules on the metal conversion speed and so on. Therefore, the anticorrosion method (or measure) of metal valve and the application of synthetic material valve have become one of the topics of the valve industry research at present.
1. Anticorrosion of metal valves is to be understood as applying a protective coating (such as paint, pigments, lubricants, etc.) on metal valves that protects them against corrosion so that the valve, whether manufactured, stored, transported or in its The entire process is not subject to corrosion.
The method of metal valve corrosion protection depends on the required protection period, shipping and storage conditions, valve construction features and materials, and of course, the economic effects of antisepsis considered.
There are 4 main methods for preserving metal valves and their parts:
1, the volatile anti-corrosion agent into the steam atmosphere (with the resistance of the paper wrapped, blowing air to suppress the passage of products through the chamber, etc.).
2, using the resistance of water and alcohol solution.
3, the anti-corrosion (protection) material coated on the valve and its parts surface.
4, the resistance of the thin film or polymer coating on the valve and its parts surface.
(Note: The current valve manufacturers, extensive use of lubricants and water resistance to dissolve the flow of anti-corrosion.)
Second, the application of material valves
Synthetic valves, which outperform metal valves in many aggressive conditions, are primarily corrosion resistant, followed by net weight, and their strength depends on the shape, alignment and number of reinforcing fibers. (In general, the greater the percentage of fiber, the greater the strength of the composite.) In valve applications, the weight content of the fibers ranges from 30% to 40% by weight, whereas the chemical stability is primarily due to the potting of the final product Fiber resin properties of the body decided. In synthetic valves, the solid polymer body can be either a thermoplastic such as PVC-PVDF, PPS-PPS, or a thermosetting resin such as polyester, ethylene and epoxy Wait). Thermosetting resins retain their strength at elevated temperatures compared to thermoplastics (ie thermosetting resins have a higher heat distortion temperature). (Note: The determination of the heat resistance of a composite during its service life is referred to as the heat distortion temperature.)
At present, the most commonly used synthetic material for chemical process valves is vinyl epoxy (thermoplastics) whose reinforcing fibers are shredded glass fibers (¼ inch long) and shredded graphite fibers (¼ inch long ). The table below compares the performance of most widely used synthetic materials with that of corrosion resistant metals.
Glass Reinforced Vinyl Graphite Reinforced Vinyl Graphite Reinforced PPS 316SS Hast-C
Tensile strength (Psi)
Bending strength (Psi) NA NA
Compressive strength (Psi)
Heat distortion temperature (° F) NA NA
Thermal expansion coefficient (in / in / ° F) 15 × 10-6
15 × 10-6
13 × 10-6
6.3 × 10-6
9.9 × 10-6
Note: NA is not applicable (or invalid)
From the surface analysis, glass and graphite reinforced composite materials compared with the metal, its tensile strength is low, therefore, synthetic material valve stress larger parts should have thick cross-section and with ribs to achieve the same with the metal performance.
Due to its corrosion resistance, high strength and light weight, synthetic valves make it an economical alternative valve product for many metal or fiberglass reinforced piping systems in corrosive service. In the chemical process conditions, excellent prospects for the use of synthetic valves.
In the valve industry, the use of organic and synthetic materials is no longer the concept of traditional metal and non-metal valve materials. Ceramic (the valve temperature can be increased from 400 ℃ to 1200 ℃ above), plastic (with anti-corrosion characteristics), synthetic materials (corrosion resistance, light weight, high strength characteristics), memory alloy Memory alloy or temperature memory alloy reversibility and high elasticity to create the valve) and so on. New materials, is developing a large number of high-performance valve with new products. The development of new technologies, so that a variety of engineering materials used in valve manufacturing has become possible.
Corrosion of metal valves and the application of synthetic material valves
Corrosion of metal valves and the application of synthetic material valves